- The micro phase separation structure of urethane resin realizes “flexible adhesion” that combines toughness and flexibility.
- We have more than 30 years of experience with adhesives for various uses such as automotive panels which requires high reliability.
- Using the primer dedicated for the respective material improves the adhesion strength to various materials.
Achieve your needs with E-TEC
--- Emulsion Technology’s environment-friendly special purpose and solvent-free materials
Urethane adhesive MIGHTYGRIP® (MIGHTY series)
Over 30 years of experience with urethane adhesives
Product outline
Property
-
Flexible adhesion
By controlling the micro phase separation structure, which is a characteristic of urethane resin, “flexible adhesion” that combines toughness and flexibility is achieved. It improves “fatigue resistance”, “impact resistance” and “peeling resistance” of the bonded structure.
-
Over 30 years experience
We have more than 30 years of experience with adhesives for various uses such as automotive outer panels that requires high adhesion reliability. The recognition of this achievement has developed and expanded a wide range of applications including housing equipment, building materials, and ships.
-
Mixing method
MIGHTY GRIP® is used by mixing two-component adhesives. Above video introduces the Bag-mixing method for small scale. We can offer cartridges, dispensers, etc. depends on your scale of use.
-
Synergistic effect with dedicated primer
Using the dedicated primer improves the adhesion strength to various materials.
This synergistic effect combines the strength of urethane adhesives with high adhesiveness and achieves the bonding between dissimilar materials such as Aluminum and CFRP. -
Total technical support for adhesion
While meeting the needs of customers in a wide range of adhesive fields, we have accumulated know-hows and technical knowledges of the urethane bonding process over the past 30 years in our history.
With the know-hows and knowledges, we can provide technical suggestion about the selection of adhesives, mass-production processes, and whatever you need.
Product lineup
| Application・Hardness | Medium-elasticity primerless adhesive for automobiles | Low elasticity | Medium elasticity | High elasticity | ||||||||||||||
| Series name | MG5000 Series | Products under development | MS1200 | MG4000A | MG3000 | MLT2900 | ||||||||||||
| Characteristics | ・ Achieves high shear strength and high peel strength | ・ Achieves high shear strength and high peel strength ・Colored black |
・ Achieves high shear strength and high peel strength ・Medium elongation, developed hardening materia |
・Adhesive with exceptional elongation and strength ・Colored black |
・Ultra-soft grade ・High impact absorption |
・High elongation at break, deformation followability ・High impact absorption |
・Achieves high shear strength and high peel strength | ・Ultra-high elasticity grade | ||||||||||
| Use | ・Exterior panel bonding for automobiles ・Battery module assembly |
・Exterior panel bonding for automobiles ・CFRP/ED steel plate, etc. |
・Exterior panel bonding for automobiles ・Type with balanced rigidity and strength |
・Exterior panel bonding for automobiles ・For applications requiring high elongation |
・Unit bath components | ・Panel water tank | ・Automatic doors | ・FRP tank | ||||||||||
| Liquid and mixing properties | Name | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | Main agent | Curing agent | |
| MG5000 | MG5030 | MG5000 | MG5032B | MG5000 | G5016-B20 | G5015-A1 | G5015-B1 | MS1200 | MS1247G | MG4000A | MG4070 | MG3000 | MG3070 | MLT2900 | ML2937S | |||
| Viscosity (Pa-s) @ 25°C | 37 | 13 | 37 | 13 | 37 | 22 | 51 | 20 | 25 | 11 | 53 | 19 | 38 | 16 | 12 | 250 | ||
| Specific gravity @ 25°C | 1.45 | 1.26 | 1.45 | 1.26 | 1.45 | 1.27 | 1.25 | 1.27 | 1.34 | 1.2 | 1.29 | 1.2 | 1.23 | 1.37 | 1.58 | 1.27 | ||
| Mixing ratio (weight) | 150 | 100 | 150 | 100 | 100 | 90 | 100 | 100 | 100 | 100 | 100 | 150 | 100 | 100 | 100 | 100 | ||
| Key colors | Yellowish-brown | White/green | Yellowish-brown | Colored black | Yellowish-brown | White/green | Light yellow | Colored black | White | White/green | White | Turquoise | Loess (yellowish-brown) | Turquoise | Beige | Colored black | ||
| Example curing conditions | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | 23°C x 3 days | ||||||||||
| Useful | 23℃ | 19 minutes | 19 minutes | 20 minutes | 10 minutes | 5 minutes | 8 minutes | 10 minutes | 80 minutes | |||||||||
| Adhesive properties | Shear strength(MPa)* | 23℃ | 18CF | 18CF | 16CF | 30ED | 2.7CF | 4.5CF | 16CF | 21CF | ||||||||
| 80℃ | 10CF | 10CF | 7CF | 7CF | 1.4CF | 2.2CF | 5.4CF | 5.0CF | ||||||||||
| -30℃ | 26CF | 26CF | 30CF | 26CF | 10CF | 20CF | 24CF | 25CF | ||||||||||
| (N/25mm)Peel strength(N/25mm) | 23℃ | 210CF | 210CF | 210CF | 180ED | 160CF | 200CF | 320CF | 260CF | |||||||||
| Resin properties | Elongation (％) | 50 | 50 | 120 | 270 | 280 | 450 | 100 | 20 | |||||||||
| Elastic modulus (MPa) | 130 | 130 | 17 | 100 | 0.3 | 3.5 | 100 | 420 | ||||||||||
| Rupture strength (MPa) | 17 | 17 | 13 | 22 | 2 | 4 | 21 | 25 | ||||||||||
| Hardness (Shore D) | 62 | 62 | 41 | 40 | 20(Shore A) | 60(Shore A) | 58 | 72 | ||||||||||
*Destructive state marker – SF: Material failure, CF： Cohesive fracture
-
*Substrate = ED-Steel , Failure mode : CF = Cohesive Failure, SF = Substrate Failure
Application
Click to open
List of Compatible Substrates
Click to open
Link
Contact
East Japan Sales Group
Specialty Chemicals Division
TEL : [81]3-6218-3841
Email : info@etec.jsr.co.jp